LF01C
Property | Unit | Typical Value | Test Method | |||
Thickness | µm | 11 | 25 | 50 | DIN 53370 | |
Tensile Strength | MD | MPa | 220 | 220 | 210 | DIN 53455-6-5 |
TD | 250 | 250 | 250 | |||
Elongation at Break | MD | % | 140 | 150 | 170 | DIN 53455-6-5 |
TD | 100 | 100 | 100 | |||
Heat Shrinkage | MD | % | 1.5 | 1.5 | 1.2 |
ASTM D1204 150℃,30min |
TD | 1.4 | 1.2 | 1.0 | |||
Friction Coefficient | µs/µk | 0.45/0.45 | 0.45/0.40 | 0.40/0.35 | DIN 53375 | |
Gloss (45o) | % | 135 | 135 | 135 | ASTM D 2457 | |
Haze | % | 2.0 | 2.0 | 2.0 | ASTM D 1003 | |
Surface Tension | Dyne/cm | 54 | 54 | 54 | ASTM D 2578 |