HC01C
WANHUA POLYESTER FILM HC01C
Product Description
HC01C is a three-layer co-extruded, bi-axially oriented film made of polyethylene terephthalate(PET). It is a high clear film with high gloss, suitable heat shrinkage and excellent processing ability, widely used for window film substrate, reflective material substrate, steel lamination and etc.
Main Properties
• Superior transparency
• High gloss
• Suitable heat shrinkage
• Excellent processing ability
Typical Value
| Property | Unit | Typical Value | Test Method | |||
| Thickness | µm | 23 | 36 | 50 | DIN 53370 | |
| Tensile Strength | MD | MPa | 220 | 220 | 210 | DIN 53455-6-5 |
| TD | 250 | 250 | 250 | |||
| Elongation at Break | MD | % | 150 | 160 | 170 | DIN 53455-6-5 |
| TD | 100 | 100 | 100 | |||
| Heat Shrinkage | MD | % | 2.0 | 2.0 | 2.0 |
ASTM D1204 150℃,30min |
| TD | 0.2 | 0.2 | 0.2 | |||
| Friction Coefficient | µs/µk | 0.45/0.45 | 0.45/0.40 | 0.40/0.35 | DIN 53375 | |
| Gloss(45o) | % | 140 | 140 | 140 | ASTM D 2457 | |
| Haze | % | 2.2 | 2.2 | 2.2 | ASTM D 1003 | |
| Surface Tension | Dyne/cm | 54 | 54 | 54 | ASTM D 2578 | |